1、中空玻璃雙組份打膠機必需在無灰塵、無溶劑污染、溫度相宜的環(huán)境中出產(chǎn),出產(chǎn)車間灰塵污染會對中空玻璃密封系統(tǒng)各個構(gòu)件的粘接效果產(chǎn)生很大的不利影響,粘接效果不好的中空玻璃制品其密封機能和功能壽命，

1, hollow glass glue machine must be produced in no dust, no solvent pollution, temperature appropriate environment, has influenced the production workshop dust pollution on the bonding effect of hollow glass sealing system of various components, insulating glass bonding effect is not good the sealing function and function of life,

2、 如果中空玻璃打膠機不夠光滑需要經(jīng)設(shè)備打磨，直到出膠正常為止。丁基膠在生產(chǎn)中不粘中空玻璃，通常原因是鋁條涂完丁基膠時間過長，造成丁基膠表面冷卻，或者是玻璃邊緣有水氣。建議涂完丁基膠要盡快合片，和調(diào)整清洗機使玻璃邊緣徹底干燥。

2, if the insulating glass polishing machine is not smooth enough, need to be polished by equipment until the glue is normal. The non stick insulating glass in the production of butyl rubber is usually due to the excessive time of the end of the butyl coating on the aluminum strip, or the cooling of the butyl rubber surface or the water vapor at the edge of the glass. It is recommended to apply butyl rubber as soon as possible and adjust the washer so that the glass edge is thoroughly dried.

3、因為溶劑的存在會導(dǎo)致丁基膠失去粘接力,從而使道密封失敗.因此,車間不要使用揮發(fā)性物質(zhì),且保持空氣通暢.

3 because the presence of solvents will lead to the loss of adhesion of butyl rubber, so that the first seal failed. Therefore, the workshop should not use volatile substances, and keep the air clear

適合的溫度是二道密封形成有效結(jié)果的必要前提,第二道密封膠供膠溫度應(yīng)盡量保證在10℃以上,只有相宜的溫度才能讓密封膠在劃定的時間內(nèi)達到使用效果,好比初始粘接力、剪切強度、彈性模量、密封機能等.

Suitable temperature is a necessary prerequisite for two seals to form an effective result, second sealant glue temperature should be kept above 10 DEG C, the temperature can only make appropriate sealant to achieve results within a specified time, such as initial adhesion, shear strength, elastic modulus, sealing performance and so on.

本文的精彩內(nèi)容來自雙組份打膠機詳細(xì)內(nèi)容請點擊我們的官方網(wǎng)站:http://linshi.jncsjx.com/謝謝您的到來!

The exciting content of this article comes from the two component dispenser, please click on our official website: http://linshi.jncsjx.com/, thank you for coming!